The dual role of coherent twin boundaries in hydrogen embrittlement | Nature Communications

Nature Communications volume 6, Article number: 6164 (2015) Cite this article

12k Accesses

178 Citations

50 Altmetric

Metrics details

This article has been updated

Hydrogen embrittlement (HE) causes engineering alloys to fracture unexpectedly, often at considerable economic or environmental cost. Inaccurate predictions of component lifetimes arise from inadequate understanding of how alloy microstructure affects HE. Here we investigate hydrogen-assisted fracture of a Ni-base superalloy and identify coherent twin boundaries (CTBs) as the microstructural features most susceptible to crack initiation. This is a surprising result considering the renowned beneficial effect of CTBs on mechanical strength and corrosion resistance of many engineering alloys. Remarkably, we also find that CTBs are resistant to crack propagation, implying that hydrogen-assisted crack initiation and propagation are governed by distinct physical mechanisms in Ni-base alloys. This finding motivates a re-evaluation of current lifetime models in light of the dual role of CTBs. It also indicates new paths to designing materials with HE-resistant microstructures.

You have full access to this article via your institution.

Uptake of hydrogen (H) can cause engineering alloys to lose their ductility and fracture unexpectedly1. This deleterious phenomenon, known as hydrogen embrittlement (HE), disrupts power generation, H containment and hydrocarbon extraction2,3,4. High-strength alloys subjected to HE in extreme environments, such as deep oil wells, are often poorly accessible and difficult to monitor, forcing reliance on conservative lifetime limits to prevent catastrophic failures5,6. Inadequate understanding of how alloy microstructure affects HE hampers higher-fidelity component lifetime predictions.

Coherent twin boundaries (CTBs) are often thought to be inherently resistant to HE because of their high surface separation energy and low H solubility7,8. However, we show that in Inconel 725—an advanced nickel (Ni)-base alloy developed specifically for extreme environments9—cracks preferentially initiate at Σ3 CTBs, yet at the same time are unlikely to propagate along them. By elucidating the surprising dual role of Σ3 boundaries in HE, our work demonstrates that H-assisted crack initiation and propagation are governed by distinct physical mechanisms in this alloy system. This finding opens new paths to improved failure prediction and to design of HE-resistant materials.

We conducted in situ tensile tests on H-charged samples of Inconel 725 in a scanning electron microscope (SEM; see Methods). The samples were prepared with different thicknesses: a thin sample (30 μm) that contains mostly through-thickness grains and a thicker sample (45 μm) where most grains do not extend through the sample thickness. No evidence of intergranular fracture was observed in samples that were not charged with H: failure in them was ductile-transgranular and occurred after onset of necking (Supplementary Fig. 1). By contrast, H-charged samples did not neck and exhibited a mixture of ductile transgranular and brittle-like intergranular fracture, as shown in Fig. 1. Such behaviour is common in HE of face-centred cubic (FCC) metals, such as Ni and Ni-base alloys10,11. In the thicker sample, we observed a large number of intergranular secondary cracks in addition to the main crack (Fig. 1a). These secondary cracks enabled us to pinpoint the microstructural features responsible for crack initiation and propagation.

(a) EBSD maps superimposed on SEM micrographs from a 45-μm-thick sample loaded to failure in tension showing both the main crack and several secondary cracks (identified by arrows). The colour map indicates out-of-plane orientations of grains. Scale bar, 100 μm. (b) Higher magnification SEM image of the boxed region in a illustrating mixed intergranular and transgranular fracture along the main crack. Scale bar, 10 μm.

To distinguish between crack initiation and propagation sites, we classify all secondary cracks as ‘single-grain boundary (GB) cracks’ or ‘multi-GB cracks,’ based on the number of cracked GBs they contain. Single-GB cracks contain just one partially or fully cracked GB, as illustrated in Fig. 2a–c, and may terminate in a short intragranular crack. Dark regions in the electron backscatter diffraction (EBSD) map represent areas with insufficient signal to determine grain orientation, due either to lack of material in the case of cracks or to surface contamination resulting from sample handling. As there are no pre-existing cracks in our samples and H-assisted cracks initiate at the sample surface12, the GBs in the single-GB cracks are identified as preferential crack initiation sites. We consider crack initiation to encompass the nucleation and initial growth of a crack along a single GB, and initiation sites to be the microstructural features at which this occurs. We do not find any intergranular crack initiation at or propagation through brittle μm-scale carbides (Supplementary Fig. 2), in contrast to previous observations in steel13, nor do we find cracks initiating along slip bands, as observed in iron-based superalloys14. After initiation, intergranular cracks may propagate along adjacent GBs and thus become multi-GB cracks, as shown in Fig. 2d–f. From these cracks, we determine which GBs are especially susceptible to crack propagation. Finally, we also investigate the character of non-cracked GBs connected to the ends of single- and multi-GB cracks. These GBs are likely to be crack propagation resistant, as cracks adjacent to them did not propagate along them.

SEM and EBSD analysis of a representative (a–c) single-GB and (d–f) multi-GB crack. (a,d) SEM micrographs with (b,e) overlaid EBSD maps are used to identify cracked and connected, non-cracked, GBs in secondary cracks. (c,f) Corresponding schematic representations. Scale bars, 5 μm.

We characterized all GBs of interest, cracked and non-cracked, by correlating SEM images with EBSD data (see Methods). GBs were classified based on their Σ value, which is a measure of misorientation in coincidence site lattice theory15. GBs with Σ=1–29 are labelled as ‘low-Σ’ and all others as ‘general.’ Among low-Σ GBs, we call particular attention to Σ3 CTBs because they are often thought to improve mechanical strength and resistance to stress corrosion cracking in metal alloys16. These qualities stem from the especially low energy of Σ3 CTBs, which is due to perfect, atom-to-atom registry between adjoining crystals at such boundaries17.

As shown in Fig. 3a, a surprisingly large fraction—19 out of 33, that is, ~58%—of single-GB cracks are along low-Σ GBs. Moreover, 13 (~40%) of them lie along Σ3 CTBs, suggesting that CTBs are preferential crack initiation sites. To assess the statistical significance of this conclusion, we compare the fraction of Σ3 CTBs in single-GB cracks with their fraction in the microstructure as a whole (Supplementary Note 1). Had cracks initiated at any GB in the microstructure with equal likelihood, then the probability or ‘P-value’ of finding 13 Σ3 CTBs at 33 single-GBs cracks would be <0.05 (Supplementary Table 1). Thus, we conclude that Σ3 CTBs are indeed preferential crack initiation sites.

Fraction of GB types that (a) initiate cracks or (b) are susceptible to crack propagation (red bars) compared with their occurrence in the baseline microstructure (grey bars). (c) Fraction of three different types of GB junctions at crack termination nodes (red bars) according to the number of low-Σ (‘Σ’) as opposed to general (‘G’) GBs that they contain compared with their occurrence in the baseline microstructure (grey bars).

To unambiguously identify the initiation site of the primary crack, we performed an in situ tensile test on a thin (30 μm) sample with through-thickness grains. All the GBs are visible on the surface of this sample and no secondary cracks are observed. The main crack initiates along a Σ3 and a Σ9 boundary, in agreement with the results reported in Fig. 3, and then quickly propagates across the sample (Supplementary Movie 1 and Supplementary Fig. 3).

To determine GB susceptibility to crack propagation, we analysed multi-GB cracks using a similar procedure to that used for crack initiation. If a specific GB type is crack-propagation resistant, we expect it to occur less frequently in multi-GB cracks than in the microstructure as a whole. Figure 3b shows that 52 out of 66 (~79%) cracked GBs in multi-GB cracks are general GBs, whereas only 14 (~21%) are low-Σ and 8 (~12%) are Σ3 CTBs. The P-values corresponding to these results are as low as ~0.03 (Supplementary Table 2), demonstrating quantitatively that the likelihood of crack propagation along low-Σ and Σ3 CTBs is indeed lower than for general GBs. Interestingly, the incidence of low-Σ GBs in multi-GB cracks is consistent with the frequency of crack initiation at low-Σ GBs, suggesting that when low-Σ GBs do appear in multi-GB cracks, it is likely that they are the initiation sites. Indeed, only 3 out of 66 multi-GB cracks contain more than one low-Σ GB.

We also analyse the GB junctions at the tips of secondary cracks (both in single- and multi-GB cracks) to assess the role of GB connectivity in crack propagation. We categorize these junctions according to the number of low-Σ boundaries among the boundaries ahead of the crack tip: zero, one or two. Figure 3c compares the types of GB junctions found at the crack tips of all 99 secondary cracks from the thicker sample with their expected occurrence in the microstructure as a whole (Supplementary Note 2). GB junctions with two low-Σ boundaries at the crack tip occur more frequently than such junctions occur in the microstructure (P-value=0.09; Supplementary Table 3). Conversely, GB junctions with no low-Σ boundaries occur less frequently at crack tips than they occur in the microstructure (P-value=0.04; Supplementary Table 3). This observation is consistent with low-Σ GBs being crack propagation resistant, and supports the notion that GB connectivity is an important factor affecting crack propagation in HE.

Previous work on pure Ni showed that increasing the fraction of low-Σ boundaries reduces HE susceptibility18. Our study reveals a more subtle relationship between microstructure and HE: low-Σ boundaries and, most surprisingly Σ3 CTBs, play a dual role in H-assisted fracture. In Inconel 725, they are weak against crack initiation and strong against crack propagation. A dramatic illustration of this duality may be seen in Fig. 4, where two distinct cracks initiate along one especially long Σ3 CTB, yet neither crack propagates far enough to fracture the GB completely. Instead, they both terminate in short intragranular cracks.

SEM micrograph illustrating the duality of Σ3 CTBs in crack initiation and propagation: two single-GB cracks (identified by red arrows) initiate along one long Σ3 CTB (dotted line). However, neither crack propagates along the entire Σ3 CTB. Instead, both cracks terminate in short intragranular segments (white circles). Scale bar, 10 μm.

The greater resistance of low-Σ GBs—and particularly Σ3 CTBs—to crack propagation, as compared with general GBs, may be due to their higher surface separation energies7 and lower H solubility8. However, the same properties might be expected to make Σ3 boundaries resistant to crack initiation, contrary to our findings. The fact that a single GB type may at the same time be a preferential crack initiation site and a poor propagation path implies that the mechanisms governing crack initiation and propagation in H-charged Inconel 725 are fundamentally different.

The mechanism by which H preferentially causes crack initiation at Σ3 CTBs has yet to be fully understood. An analogy may be made to fatigue in FCC-base alloys, where Σ3 CTBs are also found to initiate cracks19,20. Under cyclic loading, crack initiation at CTBs has been tied to localization of dislocation activity along persistent slip bands that intersect CTBs and within the boundaries themselves21,22,23. The striking similarity in the behaviour of Σ3 CTBs under fatigue and HE suggests that hydrogen induces plastic flow localization comparable to that in fatigue, even in the case of monotonic loading24. Indeed, hydrogen is well known to enhance dislocation activity25,26 and to give rise to much higher dislocation densities than would be expected based on the uniform plastic strain applied27.

To shed additional light on the role of plasticity in crack initiation, we measured the inclination angle of single-GB cracks relative to the tensile direction in our experiments. The results, shown in Fig. 5, indicate that cracks initiating on CTBs are often inclined at ~60° to the tensile axis. Therefore, under uniaxial tension, these GBs experience significant shear tractions, in addition to normal tractions. Shear loading may cause the two crystal grains that meet at the boundary to slide past each other. In the case of CTBs, such sliding may occur by dislocation glide along the GB plane, that is, by the conventional dislocation-based mechanism of plastic deformation28,29,30,31. Dislocation-mediated GB sliding is possible at CTBs because the GB plane of a CTB is a {111} plane, that is, a glide plane for dislocations in FCC metals32.

Inclination angle with respect to the tensile axis of single-GB cracks on (a) CTBs and (b) general GBs.

Enhanced dislocation activity along CTBs may promote intergranular fracture in several ways. For example, the accumulation of extrinsic dislocations increases the local hydrogen concentration and alters GB structure, elevating GB energy27,33,34,35,36. Both of these factors are expected to decrease GB cohesive energy and promote decohesion. The fact that crack initiation occurs mostly at CTBs oriented at oblique angles with respect to the tensile axis, as seen in Fig. 5, shows that some slip along the boundary is necessary before conditions favouring decohesion are established.

Another plasticity mechanism that may play a role in crack initiation is slip transmission and plastic flow localization. Previous studies have pointed to the importance of the orientation of slip systems relative to the GB plane in controlling susceptibility to integranular cracking37,38,39. In these studies, favourably oriented slip channels impinging on GBs cause incorporation of dislocations directly into the boundary plane. CTBs transmit dislocations on some slip systems easily, but constitute strong barriers to dislocation motion on others29. Dislocations that are not transmitted may remain trapped at the CTB plane. Because CTB planes are dislocation glide planes in Inconel 725, we expect that trapped dislocations are able to glide more easily within CTBs than dislocations trapped in general GBs. The high mobility of trapped dislocations at CTBs may promote the formation of dislocation substructures in the boundary plane, similar to those formed by cyclic loading within persistent slip bands21. It has been suggested that γ′ precipitates, which are present in Inconel 725 (ref. 40), may also play a role in crack initiation on Σ3 CTBs41.

The effect of dislocation plasticity on crack initiation may be far more complex when multiple cracks initiate along the same GB, as shown in Fig. 4. In such cases, different levels of crack tip shielding than at isolated cracks may be expected due to the interaction of dislocation densities surrounding neighbouring cracks42,43,44. This interaction may include—among other possibilities—enhanced annihilation of opposite sign dislocations45, generation of a greater number of statistically stored ‘redundant’ dislocations46, repulsion of like-signed dislocations and modified levels of cross-slip.

In contrast to CTBs, Fig. 5 shows that general GBs are more often found to be nearly normal to the tensile axis. Thus, failure at such boundaries is promoted predominantly by tension, rather than shearing, and classical H-induced decohesion (that is, without the influence of slip along the boundary plane) may play a more significant role in fracture. This view is consistent with the fact that slip along general GBs is typically more complex than in CTBs and may involve dislocation climb or localized shear transformations, both of which are expected to be more difficult than dislocation glide. Moreover, in contrast to CTBs, stress concentrations formed by impinging dislocations may be accommodated more easily by the more disordered atomic structure of general GBs, averting crack initiation47,48.

The identification of preferential crack initiation and propagation sites in Inconel 725 has far-reaching technological implications. Nickel-base superalloys are among the most HE-resistant structural materials in use today9 and elucidating the dual role of CTBs in HE will enable higher accuracy lifetime predictions for these materials. Our findings also indicate new paths to improving HE-resistance through microstructure design. H-induced cracks often initiate at surfaces and propagate inward12. Thus, microstructurally graded materials with few Σ3 CTBs at surfaces and a large number in the interior may be less susceptible to H-assisted fracture. Tailored densities and distributions of Σ3 CTBs may be achieved through specialized thermomechanical treatments49. Other approaches would optimize not only the number of Σ3 CTBs, but also their connectivity50, with the goal of maximizing the number of GB junctions that arrest cracks while keeping the total number of Σ3 CTBs to a minimum to reduce crack initiation. Our study also motivates a closer examination of the role GB character plays in HE in Ni-base alloys and pinpoints CTBs as key microstructural features governing HE to be studied in further detail.

Inconel 725 samples were obtained from Special Metals Corporation. Three dogbone-shaped specimens with a gage length of 15 mm and width of 1.7 mm were cut out using electrical discharge machining. They were mechanically ground to 30 and 45 μm thickness and polished on both sides to 0.04 μm with a colloidal silica suspension. After polishing, two samples were cathodically charged with hydrogen (H) for 12 h at a current density of 100 mA cm−2 in 1 N H2SO4. The third sample was tested with no hydrogen. Under these conditions, the H-charging depth is expected to be on the order of ~10 μm. These charging conditions were chosen based on a HE study in a closely related alloy12, which reported comparable mechanical behaviour (Supplementary Fig. 4).

Before testing, the sample microstructure was characterized by EBSD using a step size of 2 μm with a Philips XL30 SEM. The GB network and GB character distribution were analysed using MTex 3.4.1 in Matlab 2013b. GBs were classified according to the coincident site lattice theory using Brandon’s criterion, which sets the angular tolerance for a Σn boundary equal to (refs 51, 52). EBSD allowed to characterize all GBs at the sample surface on large areas (~1.7 × 1.9 mm2). EBSD characterization was performed both before H charging and mechanical testing as well as after the samples were tested to failure. This allowed precise correlation of the location of primary and secondary cracks with the GB network. In some cases, high-magnification scans were also acquired to resolve small secondary cracks that were not visible from large-area scans. The chemical composition of several representative GBs (a Σ3 CTB, a Σ27 and four general GBs) was analysed using Electron Dispersive Spectroscopy and Electron Energy Loss Spectroscopy in a Transmission Electron Microscope. These investigations showed no detectable segregation of impurities at any of the analysed boundaries.

In situ tensile tests were performed using a Gatan Microtest 300 tensile testing module in a JEOL 6610LV SEM. The samples were strained at a rate of ~1 × 10−4 s−1. This same testing condition was used in another HE study in a closely related alloy12. When no H was introduced, the sample failed at approximately 4.25% total engineering strain. H-charged samples failed at approximately 1.85% and 2.6% total engineering strain, for samples with thickness 30 and 45 μm, respectively. Stress–strain curves are presented in Supplementary Fig. 4.

The sample with no H did not show any evidence of intergranular fracture and failed by ductile, transgranular fracture after onset of necking (Supplementary Fig. 1). No secondary cracks were found in the sample with no H. The thicker H-charged sample (45 μm thick) exhibited more plastic deformation before failure, resulting in the formation of a large number of secondary cracks around the main crack (Fig. 1). These samples were therefore used for the statistical study of secondary cracks. The thinner H-charged sample (30 μm thick) was used to identify the initiation site of the main crack. This is evidenced in Supplementary Fig. 3, where the primary crack initiation site was identified through inspection of the in situ straining video (Supplementary Movie 1) and the post-mortem characterization of the fracture surface.

How to cite this article: Seita, M. et al. The dual role of coherent twin boundaries in hydrogen embrittlement. Nat. Commun. 6:6164 doi: 10.1038/ncomms7164 (2015).

The PDF version of this Article previously published had parts of Fig. 4 cropped, omitting necessary information. This has now been corrected in the PDF version of the Article; the HTML was correct from the time of publication.

Johnson, H. H. Hydrogen embrittlement. Science 179, 228–230 (1973).

Article ADS CAS Google Scholar

Irani, R. S. Hydrogen storage: high-pressure gas containment. MRS Bull. 27, 680–682 (2002).

Article CAS Google Scholar

Rogers, H. C. Hydrogen embrittlement of metals. Science 159, 1057–1064 (1968).

Article ADS CAS Google Scholar

Gangloff R. P., Somerday B. P. (eds)Gaseous Hydrogen Embrittlement of Materials in Energy Technologies Vol. 1, Woodhead (2012).

Louthan, M. R., Caskey, G. R., Donovan, J. A. & Rawl, D. E. Hydrogen embrittlement of metals. Mat. Sci. Eng 10, 357–368 (1972).

Article CAS Google Scholar

Shipilov, S. A. Catastrophic Failures due to Environment-Assisted Cracking of Metals: Case Histories 225–241Canadian Inst Mining, Metallurgy and Petroleum (1999).

Watanabe, T. The impact of grain boundary character distribution on fracture in polycrystals. Mat. Sci. Eng. A 176, 39–49 (1994).

Article CAS Google Scholar

Palumbo, G. & Aust, K. T. Solute effects in grain boundary engineering. Can. Metall. Quart. 34, 165–173 (1995).

Article Google Scholar

Shoemaker, L. E. Alloys 625 and 725: trends in properties and applications. inSuperalloys 718, 625, 706 and Derivatives 409–418Minerals, Metals & Materials Soc (2005).

Latanision, R. M. & Opperhauser, H. The intergranular embrittlement of nickel by hydrogen: the effect of grain boundary segregation. Metall. Trans. 5, 483–492 (1974).

Article Google Scholar

Kimura, A. & Birnbaum, H. K. Hydrogen induced grain boundary fracture in high purity nickel and its alloys—enhanced hydrogen diffusion along grain boundaries. Acta Metall. 36, 757–766 (1988).

Article CAS Google Scholar

Fournier, L., Delafosse, D. & Magnin, T. Cathodic hydrogen embrittlement in alloy 718. Mater. Sci. Eng. A Struct. Mater. Prop. Microstruct. Process 269, 111–119 (1999).

Article Google Scholar

Novak, P., Yuan, R., Somerday, B. P., Sofronis, P. & Ritchie, R. O. A statistical, physical-based, micro-mechanical model of hydrogen-induced intergranular fracture in steel. J. Mech. Phys. Solids 58, 206–226 (2010).

Article ADS CAS Google Scholar

Moody, N. R. & Robinson, S. L. The effects of hydrogen-dislocation interactions on the fracture of an iron-based superalloy. Corrosion Deformation Interactions 389–400 (1993).

Grimmer, H., Bollmann, W. & Warrington, D. H. Coincidence-site lattices and complete pattern-shift lattices in cubic crystals. Acta Crystallogr. A 30, 197–207 (1974).

Article ADS Google Scholar

Randle, V. Twinning-related grain boundary engineering. Acta Mater. 52, 4067–4081 (2004).

Article CAS Google Scholar

Wang, J., Li, N. & Misra, A. Structure and stability of Σ3 grain boundaries in face centered cubic metals. Philos. Mag. 93, 315–327 (2013).

Article ADS CAS Google Scholar

Bechtle, S., Kumar, M., Somerday, B. P., Launey, M. E. & Ritchie, R. O. Grain-boundary engineering markedly reduces susceptibility to intergranular hydrogen embrittlement in metallic materials. Acta Mater. 57, 4148–4157 (2009).

Article CAS Google Scholar

Abuzaid, W., Oral, A., Sehitoglu, H., Lambros, J. & Maier, H. J. Fatigue crack initiation in Hastelloy X—the role of boundaries. Fatigue Fract. Eng. M 36, 809–826 (2013).

Article Google Scholar

Sangid, M. D., Maier, H. J. & Sehitoglu, H. The role of grain boundaries on fatigue crack initiation—an energy approach. Int. J. Plasticity 27, 801–821 (2011).

Article Google Scholar

Déprés, C., Prasad Reddy, G. V., Tabourot, L., Sandhya, R. & Sankaran, S. in:ASME 2012 11th Biennial Conference on Engineering Systems Design and Analysis 1–10ASME (2012).

Boettner, R. C., McEvily, A. J. & Liu, Y. C. On formation of fatigue cracks at twin boundaries. Philos. Mag. 10, 95–99 (1964).

Article ADS CAS Google Scholar

Li, L. L. et al. Strain localization and fatigue cracking behaviors of Cu bicrystal with an inclined twin boundary. Acta Mater. 73, 167–176 (2014).

Article ADS CAS Google Scholar

Robertson, I. M., Lillig, D. & Ferreira, P. J. in2008 International Hydrogen Conference eds Somerday B. P., Sofronis P., Jones R. 22–37ASM International (2008).

Birnbaum, H. K. & Sofronis, P. Hydrogen-enhanced localized plasticity—a mechanism for hydrogen-related fracture. Mat. Sci. Eng. A 176, 191–202 (1994).

Article CAS Google Scholar

Robertson, I. M. The effect of hydrogen on dislocation dynamics. Eng. Fract. Mech. 68, 671–692 (2001).

Article Google Scholar

Martin, M. L., Somerday, B. P., Ritchie, R. O., Sofronis, P. & Robertson, I. M. Hydrogen-induced intergranular failure in nickel revisited. Acta Mater. 60, 2739–2745 (2012).

Article CAS Google Scholar

Li, N. et al. Twinning dislocation multiplication at a coherent twin boundary. Acta Mater. 59, 5989–5996 (2011).

Article CAS Google Scholar

Zhu, Y. T. et al. Dislocation–twin interactions in nanocrystalline fcc metals. Acta Mater. 59, 812–821 (2011).

Article CAS Google Scholar

Jin, Z. H. et al. Interactions between non-screw lattice dislocations and coherent twin boundaries in face-centered cubic metals. Acta Mater. 56, 1126–1135 (2008).

Article CAS Google Scholar

Jin, Z. H. et al. The interaction mechanism of screw dislocations with coherent twin boundaries in different face-centred cubic metals. Scripta Materialia 54, 1163–1168 (2006).

Article CAS Google Scholar

Hirth, J. P. & Lothe, J. Theory of Dislocations John Wiley & Sons (1982).

Zhu, L. et al. Modeling grain size dependent optimal twin spacing for achieving ultimate high strength and related high ductility in nanotwinned metals. Acta Mater. 59, 5544–5557 (2011).

Article CAS Google Scholar

Martin, M. L., Robertson, I. M. & Sofronis, P. Interpreting hydrogen-induced fracture surfaces in terms of deformation processes: a new approach. Acta Mater. 59, 3680–3687 (2011).

Article CAS Google Scholar

Nagao, A., Martin, M. L., Dadfarnia, M., Sofronis, P. & Robertson, I. M. The effect of nanosized (Ti,Mo)C precipitates on hydrogen embrittlement of tempered lath martensitic steel. Acta Mater. 74, 244–254 (2014).

Article CAS Google Scholar

Wang, S. et al. Hydrogen-induced intergranular failure of iron. Acta Mater. 69, 275–282 (2014).

Article CAS Google Scholar

Jiao, Z. & Was, G. S. Localized deformation and IASCC initiation in austenitic stainless steels. J. Nucl. Mater. 382, 203–209 (2008).

Article ADS CAS Google Scholar

West, E. A. & Was, G. S. Strain incompatibilities and their role in intergranular cracking of irradiated 316 l stainless steel. J. Nucl. Mater. 441, 623–632 (2013).

Article ADS CAS Google Scholar

Seal, J. R., Crimp, M. A., Bieler, T. R. & Boehlert, C. J. Analysis of slip transfer and deformation behavior across the α/β interface in Ti–5Al–2.5Sn (wt.%) with an equiaxed microstructure. Mat. Sci. Eng. A 552, 61–68 (2012).

Article CAS Google Scholar

Wang, M. S., Hanson, J. P., Gradečak, S. & Demkowicz, M. J. Cutting apart of gamma double prime precipitates by dislocations emitted from nanoscale surface notches in Ni-base alloy 725. Mater. Res. Lett 1, 77–80 (2013).

Article Google Scholar

Chen, S., Zhao, M. & Rong, L. Hydrogen-induced cracking behavior of twin boundary in gamma prime phase strengthened Fe—Ni based austenitic alloys. Mat. Sci. Eng. A 561, 7–12 (2013).

Article CAS Google Scholar

Zielinski, W., Lii, M. J. & Gerberich, W. W. Crack-tip dislocation emission arrangements for equilibrium —I. In situ TEM observations of Fe2wt%Si. Acta Metall. Mater 40, 2861–2871 (1992).

Article CAS Google Scholar

Huang, H. & Gerberich, W. W. Crack-tip dislocation emission arrangements for equilibrium—II. Comparisons to analytical and computer simulation models. Acta Metall. Mater 40, 2873–2881 (1992).

Article CAS Google Scholar

Marsh, P. G., Zielinski, W., Huang, H. & Gerberich, W. W. Crack-tip dislocation emission arrangements for equilibrium—III. Application to large applied stress intensities. Acta Metall. Mater 40, 2883–2894 (1992).

Article CAS Google Scholar

Shu, J. Y., Fleck, N. A., Van der Giessen, E. & Needleman, A. Boundary layers in constrained plastic flow: comparison of nonlocal and discrete dislocation plasticity. J. Mech. Phys. Solids 49, 1361–1395 (2001).

Article ADS Google Scholar

Weertman, J., Lin, I. H. & Thomson, R. Double slip plane crack model. Acta Metall. 31, 473–482 (1983).

Article Google Scholar

Priester, L. ‘Dislocation-interface’ interaction—stress accommodation processes at interfaces. Mater. Sci. Eng. A Struct. Mater. Prop. Microstruct. Process 309, 430–439 (2001).

Article Google Scholar

Caturla, M. J., Nieh, T. G. & Stolken, J. S. Differences in deformation processes in nanocrystalline nickel with low- and high-angle boundaries from atomistic simulations. Appl. Phys. Lett. 84, 598–600 (2004).

Article ADS CAS Google Scholar

Lehockey, E. M. & Palumbo, G. On the creep behaviour of grain boundary engineered nickel. Mat. Sci. Eng. A 237, 168–172 (1997).

Article Google Scholar

Kumar, M., King, W. E. & Schwartz, A. J. Modifications to the microstructural topology in f.c.c. materials through thermomechanical processing. Acta Mater. 48, 2081–2091 (2000).

Article CAS Google Scholar

King, A. H. & Shekhar, S. What does it mean to be special? The significance and application of the Brandon criterion. J. Mater. Sci. 41, 7675–7682 (2006).

Article ADS CAS Google Scholar

Brandon, D. G. The structure of high-angle grain boundaries. Acta Metall. 14, 1479–1484 (1966).

Article CAS Google Scholar

Download references

This work was supported by the BP-MIT Materials and Corrosion Center. We are grateful to Sai Venkateswaran for useful discussions, to Oliver K. Johnson for helping develop MATLAB codes for microstructural analysis and to Eric J. Jones for performing Transmission Electron Microscope measurements. We are also grateful to Junjie Niu and Sangkwon Lee for help with hydrogen charging and to Donald Galler for help with the tensile testing module. Access to shared experimental facilities was provided by the MIT Center for Materials Science Engineering, supported in part by the MRSEC Program of the National Science Foundation under award number DMR—0213282. J.P.H. acknowledges the Department of Energy Office of Science Graduate Fellowship Program (DOE SCGF), made possible in part by the American Recovery and Reinvestment Act of 2009, administered by ORISE-ORAU under contract no. DE-AC05-06OR23100.

Matteo Seita and John P. Hanson: These authors contributed equally to this work

Department of Materials Science and Engineering, Massachusetts Institute of Technology, Cambridge, 02139, Massachusetts, USA

Matteo Seita, Silvija Gradečak & Michael J. Demkowicz

Department of Nuclear Science and Engineering, Massachusetts Institute of Technology, Cambridge, 02139, Massachusetts, USA

John P. Hanson

You can also search for this author in PubMed Google Scholar

The project was planned and supervised by M.J.D. and S.G. The experimental design was conceived by M.S., and the statistical testing was conceived by J.P.H. Experiments, data collection and analysis were performed by M.S. and J.P.H. and discussed by M.S., J.P.H., M.J.D. and S.G. The manuscript was prepared by M.S., J.P.H., M.J.D. and S.G.

Correspondence to Silvija Gradečak or Michael J. Demkowicz.

The authors declare no competing financial interests.

Supplementary Figures 1-4, Supplementary Tables 1-3, Supplementary Notes 1-2, and Supplementary Reference (PDF 973 kb)

In situ tensile test of hydrogen embrittled Inconel 725. The SEM movie shows the in situ tensile test of the H-charged thin sample (30 μm) and the exact location of the primary crack initiation site, which consist of a CTB and a Σ9 GB. (MOV 7405 kb)

Reprints and permissions

Seita, M., Hanson, J., Gradečak, S. et al. The dual role of coherent twin boundaries in hydrogen embrittlement. Nat Commun 6, 6164 (2015). https://doi.org/10.1038/ncomms7164

Download citation

Received: 03 July 2014

Accepted: 22 December 2014

Published: 05 February 2015

DOI: https://doi.org/10.1038/ncomms7164

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

Journal of Materials Engineering and Performance (2023)

The International Journal of Advanced Manufacturing Technology (2023)

Journal of Materials Science (2022)

Scientific Reports (2021)

npj Materials Degradation (2021)